Efeito da carga e do tamanho do grão abrasivo no desgaste do ferro fundido branco 19,9 % cromo e 2,9 % carbono
Nenhuma Miniatura disponível
Data
2013-04-01
Autores
Tozetti, Karla Dubberstein
Título da Revista
ISSN da Revista
Título de Volume
Editor
Universidade Federal do Espírito Santo
Resumo
In this research, the effects of different applied load and abrasive size on the martensitic high-chromium write cast iron (with a chemical composition: 2,9% carbon and 19,9% chromium) abrasive wear was investigated. The alloy s microstructure consists of: a matrix martensite tempered at 200 ° C with eutectic carbide. Abrasive wear tests using a pin test on silica and garnet paper were carried out using three different abrasives sizes: 63 μm, 149 μm e 177 μm and two applied load: 5 N e 10 N. And the rubber wheel abrasion test (ASTM standard G-65) was carried out using three abrasives sizes: 87 μm, 115 μm e 170 μm and three distinct applied loads: 44 N, 80 N e 130 N. The specimens wear surface was examined by scanning electron microscopy (SEM) for identifying the wear mechanism. The rubbers wheel abrasion test results show that: the mass loss of the write cast iron alloy increases linearly with the increase of particle size until the critical particle size is reached. In pin test on silica paper, to the largest abrasive size, the lost volume in abrasion tripled with applied load increasing of 5 N to10 N. In general, the mass loss increases with the increase of the load applied and the abrasive size.
Descrição
Palavras-chave
High-chromium white cast iron , Abrasive size , Load , Abrasive wear , Pin on disc , Rubber wheel , Tamanho da partícula abrasiva , Carga , Desgaste abrasivo , Pino sobre lixa , Roda-de-borracha
Citação
TOZETTI, Karla Dubberstein. Efeito da carga e do tamanho do grão abrasivo no desgaste do ferro fundido branco 19,9 % cromo e 2,9 % carbono. 2013. 121 f. Dissertação (Mestrado em Engenharia Mecânica) - Universidade Federal do Espírito Santo, Centro Tecnológico, Vitória, 2013.