Caracterização estrutural dos compostos Ca2MnReO6 e Ca1,8Ce0,2MnReO6 através da técnica de absorção de raio X
Nenhuma Miniatura disponível
Data
2014-11-24
Autores
Rodrigues, Erika Laurina Oliveira
Título da Revista
ISSN da Revista
Título de Volume
Editor
Universidade Federal do Espírito Santo
Resumo
In this work will be presented a description about the synthesis methodsusing solid state reaction using the encapsulated quartz tube technique and a description about the morphogolical and strutural characteristics of the compounds Ca2MnReO6and Ca1,8Ce0,2MnReO6. The analysis of the diffraction patternusing Rietveld show us that the dopped sample doped with 5% cerium is monophasic to and it was also possible to note an expansion of the unit cell without changing the symmetry of the doped sample. The electron microscopy images showed a homogeneous size and shape of the particles in the sample. The measurements of X-ray absorption by synchrotron radiation at the edge K of Mnand the edge L3of Reshow that both elements have mixed valence in samples with and without doping , assuming a value for Re+7 in the doped , while the change was not observed value the valence of Mn.
Descrição
Palavras-chave
Double peroviskite , X-ray diffraction (XRD) , Scanning electron microscopy , Cerium doping , Peroviskitas duplas , XANES , EXAFS , Difração de raio X , Microscopia de varredura eletrônica , Dopagem com cério
Citação
RODRIGUES, Erika Laurina Oliveira. Caracterização estrutural dos compostos Ca2MnReO6 e Ca1,8Ce0,2MnReO6 através da técnica de absorção de raio X. 2014. 63 f. Dissertação (Mestrado em Física) – Programa de Pós-Graduação em Física, Universidade Federal do Espírito Santo, Centro de Ciências Exatas e da Terra, Vitória, 2014.